A new type of burnt lime slaker have been developed by LAIGANG sintering plant.

莱钢结厂研制了一种新型的生石灰消化器。

The process conditions,including presintering temperature,sintering temperature and time,cooling mode and pretreatment were studied.

对成过(预温度、结温度及保温时间、降温方式)及预处理艺进行了研究。

Modified polyacrylic acid aqueous vehicle may be the headmost applied in electronic pastes of high sintering temperature.

其改性聚丙烯酸将有可能在高温电子浆料率先应用。

A white powder,coarse particles and mealiness ,hardly souble in acidic or alkaline solutions,with stable chemical property and good sintering performance.

外观呈白色粗颗粒或微种，难溶于酸或碱液，化学性能稳定，具有良好的结性能。

Addition of partial nephelite during bauxite sintering could not only make up consumption of soda, but also attain purpose for treating nephelite.

在铝土矿结过添加部分霞石矿,以补充碱的消耗,同时达到处理霞石的目的。

The author introducd the electric equipment design of ore smelting eutecticum engineering of ore sintering plate, stated the problemes and the countermeasures.

介绍了矿冶共晶结车间的电气设计,并阐述了设计遇到一些问题以及解决的方法。

Using dolomite and sinter magnesia clinker as a main material and added with alkali metal phosphate binder and additives,amagnesia-calcia coating material has been developed.

采用白云石配以适量的镁砂熟料和磷酸盐结合剂及复合外加剂研制出了具有较好性能的镁钙质间包涂料。

The effects of sintering parameters on the shear and bond strength of ceramet friction material were studied and its fracture morphology was observed and analyzed.

研究了结艺参数对金属陶瓷摩擦材料抗剪强度和金属陶瓷摩擦片结合强度的影响,观察并分析了断口形貌。

The color of the products is argent grey metallic shine, smooth, unknit. They mustn't be oxydic badly, lacking of sintering, over heating, delamination and cracking.

产品表面呈银灰色金属光泽、光滑、平整、不得有严重氧化现象，不得有欠、过熔、鼓泡、分层、裂纹等缺陷。

The obtained achievement in building material industry is studied, including sintering cement with substituting coal by cokeite and smelting rockwool with substituting coke by cokeite and so on.

本文介绍了采煤副产品～天然焦的特性，并对其在建材行业的开发研究成果进行了评述．主要包括天然焦代煤制水泥，天然焦代焦炭熔制岩棉等。

The metal reflet glaze samples were prepared with the Huxian wheat-meal-stone accession 0%, 5%, 10% and 15% according to the traditional metal reflet glaze formula and then sintered at 950%.

摘要在金属光泽釉配方基础上，制作了4组户县麦饭石添量为0%，5%，10%，15%的金属光泽釉试样，在950℃温度环境下成。

For sinter with 25% and 50% MAC fines the iron oxides mainly consisted of hematite and magnetite, the bonding phase were mainly dicalcium silicate, glassiness, and a few amount of calcium ferrite.

配比为25%和50%的种结矿铁氧化物均以赤铁矿、磁铁矿为主，粘结相主要以铁酸钙、硅酸二钙和玻璃质为主，但铁酸钙数量不多。